| 尼龙6各牌号 | Grade | TP-S62 | TP-S65 | TP-S67K | TP-S68 | TP-S69 | ||||
| 磁気特性 Magnetic Properties | Toda NO. 610-1 | 残留磁束密度 | Residual flux density | Br | mT | 239 | 275 | 290 | 292 | 308 |
| (G) | (2390) | (2750) | (2900) | (2920) | (3080) | |||||
| 保磁力 | Coercive Force | bHc | kA/m | 170 | 187 | 180 | 185 | 183 | ||
| (Oe) | (2140) | (2350) | (2280) | (2320) | (2300) | |||||
| 保磁力 | Intrinsic Coercivity | iHc | kA/m | 230.8 | 221.2 | 210.9 | 215 | 207 | ||
| (Oe) | (2900) | (2780) | (2650) | (2700) | (2600) | |||||
| 最大磁能积 | Maximum Energy Product | (BH)max | kJ/m3 | 11.14 | 14.88 | 16.5 | 16.9 | 18.7 | ||
| (MGOe) | (1.40) | (1.87) | (2.07) | (2.13) | (2.35) | |||||
| 物理特性 Physical Properties | ASTM-D792 | 成形密度 | Mold Density | g/cm3 | 3.27 | 3.63 | 3.73 | 3.77 | 3.87 | |
| ASTM-D1238 | 流動性 | Melt Flow Rate | MI | g/10min | 100 | 135 | 70 | 85 | 75 | |
| Condition | 270℃/10kg | 270℃/10kg | 270℃/10kg | 270℃/10kg | 270℃/10kg | |||||
| ASTM-D790 | 弯曲强度 | Flexural Strength | MPa | 189 | 167 | 182 | 163 | 177 | ||
| (kg/cm2) | (1927) | (1703) | (1856) | (1662) | (1805) | |||||
| 弯曲弹性率 | Flexural Modulus | GPa | 15.8 | 23.0 | 27.5 | 26.9 | 29.5 | |||
| (kg/cm2) | (1.6E+05) | (2.3E+05) | (2.8E+05) | (2.7E+05) | (3.0E+05) | |||||
| ASTM-D638 | 拉伸强度 | Tensile Strength | MPa | 99.5 | 79.1 | 97.6 | 90.0 | 90.0 | ||
| (kg/cm2) | (1015) | (807) | (995) | (918) | (918) | |||||
| 伸展 | Elongation | % | 4.6 | 3.0 | 3.4 | 3.3 | 2.8 | |||
| ASTM-D256 | 冲击强度 | IZOD Impact Strength | kJ/m2 | NB | 11.9 | 13.5 | 10.1 | 11.5 | ||
| (kgf･cm/cm2) | (NB) | (12.1) | (13.7) | (10.3) | (11.7) | |||||
| Toda Method | 收缩率 | Shrinkage | % | 0.75 | 0.57 | 0.41 | 0.44 | 0.45 | ||
| UL 94 | 难燃性 | UL Flammability | class | --- | --- | --- | --- | --- | ||
| JIS K7197 | 线膨胀系数 | Liner Expantion | 1/℃ | 4.5E-05 | 3.4E-05 | --- | 3.7E-05 | --- | ||
| ASTM-D648 | 热变形温度 | Deflection Temp. | ℃ | --- | --- | --- | 172 | --- | ||
| 射出成形 Injection Parameters | 预备干燥 | Predrying | ℃ / hr | 120 / 3 | 120 / 3 | 120 / 3 | 120 / 3 | 120 / 3 | ||
| Toda Method | 气缸 温度 | Barrel Temp. | H1 | ℃ | 270 | 265 | 270 | 265 | 265 | |
| JSW J20M II | H2 | ℃ | 310 | 310 | 310 | 300 | 310 | |||
| (20ton) | HN | ℃ | 305 | 305 | 305 | 300 | 305 | |||
| 模具温度 | Mold Temp. | ℃ | 100 | 100 | 100 | 100 | 100 | |||
| DUMBBELL | 设定压力 | Pressure | P% | 51 | 42 | 58 | 52 | 64 | ||
| L : 175mm | 设定速度 | Speed | V% | 70 | 70 | 70 | 70 | 70 | ||
| W : 12.5mm | 射出压力结果 | Pressure (Result) | MPa | 128.6 | 106.7 | 147.3 | 129.6 | 144.1 | ||
| T : 3.2mm | (kg/cm2) | (1312) | (1088) | (1502) | (1321) | (1470) | ||||